Perpendicular-to-crack chloride ingress in cracked and autonomously healed concrete
Van Belleghem, B.; Van den Heede, P.; Van Tittelboom, K.; De Belie, N. (2018). Perpendicular-to-crack chloride ingress in cracked and autonomously healed concrete. MATEC Web of Conferences 199: 02011. https://hdl.handle.net/10.1051/matecconf/201819902011
In: MATEC Web of Conferences. EDP Sciences: France. e-ISSN 2261-236X, more

Available in  Authors 

Authors  Top 
  • Van Belleghem, B., more
  • Van den Heede, P., more
  • Van Tittelboom, K., more
  • De Belie, N., more

Abstract
    Cracks in reinforced concrete structures exposed to a marine environment or dc-icing salts can cause major durability issues due do accelerated ingress of chloride ions. In this study, the influence of autonomous crack healing by means of encapsulated polyurethane on the chloride ingress perpendicular to cracks was evaluated. This was done quantitatively by determining perpendicular-to-crack chloride profiles by means of profile grinding followed by potentiometric titration and qualitatively through visualization of the chloride penetration front by means of the AgNO3 spray method. The resulting chloride profiles showed that the healing mechanism was able to reduce the chloride concentrations in the direct vicinity of the crack to a large extent and to reduce the perpendicular-to-crack chloride penetration, especially further away from the exposed surface. Visualization of the chloride penetration front showed some variation in crack healing. For some healed samples almost no additional chloride ingress was found compared to uncracked samples, others showed a slightly enhanced ingress at the crack location but less perpendicular-to crack chloride penetration compared to untreated cracked samples. Generally, the reduced amount of chlorides present in the concrete matrix due to crack healing will enhance the durability and service life of concrete structures.