Durability of an adhesively bonded joint between steel ship hull and sandwich superstructure pre-exposed to saline environment
Jaiswal, P.R.; Kumar, R.I.; Mouton, L.; Starink, L.; Katsivalis, I.; Cedric, V.; De Waele, W. (2024). Durability of an adhesively bonded joint between steel ship hull and sandwich superstructure pre-exposed to saline environment. J. Adhes. Latest Articles: 30. https://dx.doi.org/10.1080/00218464.2023.2282162
In: The Journal of Adhesion. Gordon and Breach/Taylor & Francis: New York. ISSN 0021-8464; e-ISSN 1545-5823, meer
Peer reviewed article  

Beschikbaar in  Auteurs 

Trefwoord
    Marien/Kust
Author keywords
    MMA adhesive; marine environment; tensile; fatigue; strain; damage characterisation

Auteurs  Top 
  • Jaiswal, P.R., meer
  • Kumar, R.I., meer
  • Mouton, L.
  • Starink, L.
  • Katsivalis, I.
  • Cedric, V.
  • De Waele, W., meer

Abstract

    This paper outlines an experimental investigation into the durability of large-scale adhesively bonded joints with a thick layer of methyl methacrylate adhesive (MMA). Ageing has been performed by immersion in a 3.5 wt% NaCl solution for 10 weeks at 50°C. Two aged and one unaged specimen were subjected to tensile testing, and three aged and one unaged specimen were loaded up to ~ 3.5 million fatigue cycles followed by a residual tensile test. The ductility of the adhesive is affected by ageing and fatigue testing. Despite a decrease in ductility, the plastic zone development was adequate for the required strain redistribution without compromising the joint performance (strength and stiffness) demonstrating the fatigue tolerance of the joint. The shear, longitudinal, and peel strain values in the adhesive bulk are evaluated by digital image correlation. The shear strength values are significantly higher than the requirements following from the design. All specimens failed by sudden delamination of the composite plate. Post-mortem analysis showed no corrosion travel at the interface of steel and adhesive.